[1]陈辉明,李明茂,汪建华,等.低氧铜杆线铜粉剥离原因分析及其对策措施[J].有色金属科学与工程,2016,(05预):785-789.
 CHEN Huiming,LI Mingmao,WANG Jianhua,et al.Research and countermeasures on flaking principle of copper rod and copper wire surfaces copper flakes[J].,2016,(05预):785-789.
点击复制

低氧铜杆线铜粉剥离原因分析及其对策措施(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2016年05期预
页码:
785-789
栏目:
出版日期:
2016-10-31

文章信息/Info

Title:
Research and countermeasures on flaking principle of copper rod and copper wire surfaces copper flakes
作者:
陈辉明1李明茂1汪建华2朱映玉3陈广军3
(1. 江西理工大学国家铜冶炼及加工工程技术研究中心,江西 赣州,341000;2. 江西铜业集团铜材有限公司,江西 贵溪,335424;3. 江西理工大学材料科学与工程学院, 江西 赣州, 341000)
Author(s):
CHEN Huiming1 LI Mingmao1 WANG Jianhua2 ZHU Yingyu3 CHEN Guangjun3
(1.National Copper Metallurgy and Process Engineering Research Center, Jiangxi University of Science and TechnologyGanzhou 341000,China; 2.Jiangxi Copper Product Co.,Ltd.,, Guixi 335424,China; 3. School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China)
关键词:
铜粉氧化膜表面损伤拉丝模具
分类号:
-
DOI:
-
文献标志码:
-
摘要:
表面铜粉剥离,导致铜杆线表面损伤,其对铜杆线拉伸过程具有较大影响。通过扫描电镜分析,剥离铜粉厚度可达25μm,经物相分析确定其主要成分为铜及铜的氧化物。通过对剥离物和杆线表面缺陷进行形貌分析,以铜杆线的生产、加工各环节作为研究对象,并确认了铜杆轧制工艺、无酸清洗工艺、线表擦伤、拉伸角度及拉丝模具等五方面影响因素,并制定了相应的对策措施。研究表明,铜杆氧化物剥落和机械损伤是铜粉剥离的主要原因,在铜杆线生产、加工环节,防止氧化物带入铜基体和避免铜线表面损伤能有效减少铜杆线铜粉剥离。

参考文献/References:

[1] 强宗良,崔养户.金属拉伸过程中的拉伸应力及影响因素[J].有色金属加工, 2003,32(6):19-22.
[2] 李明茂,杨斌,袁静.单晶铜线在强冷变形过程中的组织性能转变[J].特种铸造及有色合金. 2011,31(12):1087-1090.
[3] Ma X, Lapovok R, Gu C, et al. Deep drawing behaviour of ultrafine grained copper: modelling and experiment[J]. Journal of materials science, 2009, 44(14): 3807-3812.
[4] 郑颖.探讨漆包线生产对铜导体质量的要求[J].电线电缆,2013,1:17-20.
[5] 凌春华,李福.漆包线生产工艺及技术的新进展[J].电线电缆,2010,2:1-3.
[6] 蒋大伟,李鸿岩,翟龙,等.一种耐高温漆包线的制备与工艺研究[J]. 绝缘材料.2013,46(3):14-16.
[7] 樊良子,虞鑫海,吴爽,等.耐高温漆包线漆的研究进展[J].绝缘材料.2012,45(1):30-33.
[8] 芮斌,向启联,盛 兴,等.新型铜线拉丝润滑剂的研制[J].润滑与密封,2010,35(7):100-102.
[9] Hofmann H, Marcantoni G. Copper Wire-Drawing Lubricants[J]. Encyclopedia of Lubricants and Lubrication, 2014: 324-336.
[10] FU Y B, CHEN J, LIU N, et al. Study of ultrahigh-purity copper billets refined by vacuum melting and directional solidification[J]. Rare Metals, 2011(3):304-309.
[11] 居敏刚,郭均华.SCR连铸连轧铜杆生产线温度的控制[J].铜加工,2005,99(3):30-33.
[12] 罗欣.抗电晕漆包线的研制及激励探讨[J].铜业工程.2012,114(2):1-4.
[13] Kovács S, Mertinger V. Development of a complex optimizing model of wire drawing technology[C]//Materials Science Forum. 2013, 752: 125-134.
[14] 李明茂,汪建华,袁静.超细铜线拉制过程中断线原因分析与对策[J].特种铸造及有色合金,2012,32(6):583-586.
[15] 孙建林.轧制工艺润滑原理、技术与运用[M].北京:冶金工业出版社,2010.
[16] 李小玉.轧制工艺润滑[M].北京:冶金工业出版社,1981.

相似文献/References:

[1]蔡报珍.超细铜粉的制备及应用[J].有色金属科学与工程,2008,(04):42.
 CAI Bao-zhen.Preparation and Application of Ultra-fine Copper Powder[J].,2008,(05预):42.
[2]肖志华a,廖春发b,王旭b,等.熔盐电解制备铜粉的实验研究[J].有色金属科学与工程,2012,(06):28.
 XIAO Zhi-huaa,LIAO Chun-fab,WANG Xub,et al.Experimental study of the preparation of copper powder through molten salt electrolysis[J].,2012,(05预):28.
[3]肖志华,廖春发,王旭,等.熔盐电解制备铜粉的实验研究[J].有色金属科学与工程,2016,(05预):1360.
 XIAO Zhi-hua,LIAO Chun-fa,WANG Xu,et al.Experimental study of molten salt electrolysis Copper Powder Preparation[J].,2016,(05预):1360.
[4]周珂ab,林高用ab,刘伯康,等.Cu-Zn合金金色表面膜的色泽特性和抗变色性研究[J].有色金属科学与工程,2017,(01):63.[doi:10.13264/j.cnki.ysjskx.2017.01.011]
 ZHOU Keab,LIN Gaoyongab,LIU Bokang,et al.Color characteristics and anti-tarnish property of gold film of Cu-Zn alloy[J].,2017,(05预):63.[doi:10.13264/j.cnki.ysjskx.2017.01.011]
[5]陈辉明a,李明茂a,汪建华,等.低氧铜杆线铜粉剥离原因分析及其对策措施[J].有色金属科学与工程,2014,(06):83.[doi:10.13264/j.cnki.ysjskx.2014.06.014]
 CHEN Huiminga,LI Mingmaoa,WANG Jianhua,et al.Cause analysis and countermeasures of exfoliation of copper powders on copper rod and wire[J].,2014,(05预):83.[doi:10.13264/j.cnki.ysjskx.2014.06.014]

备注/Memo

备注/Memo:
-
更新日期/Last Update: 2016-04-01