|本期目录/Table of Contents|

[1]卢智成,李永亮,朱茂华,等.Al含量对Pb-Al合金耐腐蚀性能的影响[J].有色金属科学与工程,2015,(05):52-56.[doi:10.13264/j.cnki.ysjskx.2015.05.010]
 LU Zhicheng,LI Yongliang,ZHU Maohua,et al.Effect of Al content on the corrosion resistance of Pb-Al alloys[J].,2015,(05):52-56.[doi:10.13264/j.cnki.ysjskx.2015.05.010]
点击复制

Al含量对Pb-Al合金耐腐蚀性能的影响(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2015年05期
页码:
52-56
栏目:
出版日期:
2015-10-20

文章信息/Info

Title:
Effect of Al content on the corrosion resistance of Pb-Al alloys
作者:
卢智成1 李永亮2 朱茂华2 李茂旺3 刘振林1 杨占兵2 王福明2
1.中国电力科学研究院,北京 100192;2.北京科技大学冶金与生态工程学院,北京 100083;3.江西冶金职业技术学院,江西 新余 338015
Author(s):
LU Zhicheng1 LI Yongliang2 ZHU Maohua2 LI Maowang3 LIU Zhenlin2YANG Zhanbing2 WANG Fuming2
1. China Electric Power Research Institute, Beijing 100192, China; 2. School of Metallurgrical and Ecological Engineering,University of Science and Technology Beijing, Beijing 100083, China;3. Jiangxi Metallurgical Vocational and Technical College, Xinyu 338015, China
关键词:
铅铝合金铅含量耐腐蚀性盐雾实验
分类号:
TG146.2;TF125.2
DOI:
10.13264/j.cnki.ysjskx.2015.05.010
文献标志码:
A
摘要:
利用盐雾腐蚀实验,研究铝(Al)含量对铅铝(Pb-Al)二元合金耐腐蚀性能的影响.试样腐蚀后的重量损失反映合金的耐腐蚀性能,当Al的含量(指质量百分含量,下同)为0.05 %和0.10 %时,Pb-Al合金的失重较小,说明其耐腐蚀性能比纯铅有明显提高.进一步提高Al含量至0.15 %,Pb-Al合金的耐腐蚀性无明显改善.利用光学显微镜观察了腐蚀后显微形貌的变化,Al的含量为0.05 %和0.10 %时,测试面的腐蚀沟和点蚀坑数量少且尺寸较小,而当Al含量为0和0.15 %时,腐蚀沟和点蚀坑的数量和尺寸均较大,此时合金的耐腐蚀性能也相对较差.

参考文献/References:

[1] 张雪松,代泽兵,曹枚根,等.安装新型铅减震器的220kV断路器振动台试验[J].高压电器,2011(8):14-17.
[2] 尤红兵,赵凤新.加载频率对铅合金减震器动力特性的影响[J].震灾防御技术,2011(4):384-395.
[3] 尤红兵,赵凤新.铅合金减震器在SF_6断路器减震中的应用[J].电网技术,2010(11):221-226.
[4] 姚维义,彭可,唐谟堂,等.铅锭白锈形成机理[J].中南大学学报(自然科学版),2004,35(1):54-58.
[5] 王永红,鹿中晖,李英志,等.三种不同土壤中金属的腐蚀特性比较[J].腐蚀科学与防护技术,2010(5):461-463.
[6] 姚维义,唐谟堂,彭可,等.铸造铅腐蚀机理的研究[J].腐蚀科学与防护技术,2004(4):203-206.
[7] Mohanty U S, Lin K. The polarization characteristics of Pb-free Sn-8.5Zn-XAg-0.1Al-0.05Ga alloy in 3.5% NaCl solution[J]. Corrosion Science, 2007,49(7):2815-2831.
[8] 刘振林,李永亮,朱茂华,等.铝含量对铅力学性能的影响[J].有色金属科学与工程,2015,6(2):37-41.
[9] Mohanty U S, Lin K. Electrochemical corrosion behaviour of Pb-free Sn-8.5Zn-0.05Al-XGa and Sn-3Ag-0.5Cu alloys in chloride containing aqueous solution[J]. Corrosion Science, 2008,50(9):2437-2443.
[10] Mohanty U S, Lin K. Effect of Al on the electrochemical corrosion behaviour of Pb free Sn-8.5 Zn-0.5 Ag-XAl-0.5 Ga solder in 3.5% NaCl solution[J]. Applied Surface Science, 2006,252(16):5907-5916.
[11] Wang N, Wang R, Peng C, et al. Corrosion behavior of Mg-Al-Pb and Mg-Al-Pb-Zn-Mn alloys in 3.5% NaCl solution[J]. Transactions of Nonferrous Metals Society of China, 2010,20(10):1936-1943.
[12] Yang H, Liu H, Zhang Y, et al. Properties of a new type Al/Pb-0.3%Ag alloy composite anode for zinc electrowinning[J]. International Journal of Minerals, Metallurgy, and Materials, 2013,20(10):986-993.
[13] 唐有根,贺小红,杨习文,等.添加铈对低锑铅合金的微观结构及电化学性能的影响[J].中国稀土学报,2007(3):323-328.
[14] 鲁俐.高强铅基合金组织与性能研究[D].昆明:昆明理工大学,2009.
[15] 李宁,黎德育,翟淑芳,等.铅合金的组成与浇铸方法及其耐蚀性[J].电池,2001(5):209-211.
[16] 森孝夫,唐明达.铅锌合金的最新开发动向[J].有色金属加工,1997(4):55-65.
[17] Osório W R, Peixoto L C, Garcia A. The effects of Ag content and dendrite spacing on the electrochemical behavior of Pb-Ag alloys for Pb-acid battery components[J]. Journal of Power Sources, 2013,238:324-335.
[18] 宋高阳,宋波,杨玉厚,等.利用超重力分离5052铝合金熔体中的非金属夹杂[J].有色金属科学与工程,2015,6(1):29-34.

相似文献/References:

[1]刘振林,卢智成,李永亮,等.Al含量对变形铅室温再结晶行为的影响[J].有色金属科学与工程,2016,(05预):165.
 LIU Zhenlina,LU Zhichenga,LI Yongliangb,et al.Effect of Al content on the recrystallization behavior of lead at room temperature[J].,2016,(05):165.
[2]刘振林,卢智成,李永亮,等.Al含量对变形铅室温再结晶行为的影响[J].有色金属科学与工程,2016,(03):35.[doi:10.13264/j.cnki.ysjskx.2016.03.007]
 LIU Zhenlin,LU Zhicheng,LI Yongliang,et al.Effect of Al content on re-crystallization behavior of lead at room temperature[J].,2016,(05):35.[doi:10.13264/j.cnki.ysjskx.2016.03.007]

备注/Memo

备注/Memo:
收稿日期:2015-05-11基金项目:国家自然科学基金资助项目(51374018,51174020)作者简介:卢智成 (1978- ),男,博士,主要从事电网抗震与减隔震技术方面的研究,E-mail: luzc@epri.sgcc.com.cn.通信作者:王福明 (1963- ), 男,教授,博导,主要从事钢铁冶金基础理论,钢中合金化与相变,钢种开发等研究,E-mail:wangfuming@metall.ustb.edu.cn.
更新日期/Last Update: 2015-10-30