 TONG Zhifang,JIANG Xiyuan,CHEN Tao.Effect of composition on sulfur partition ratio between CaO-Al2O3-SiO2-TiO2-MgO-Na2O slags and hot iron[J].,2016,(01):5-10.[doi:10.13264/j.cnki.ysjskx.2016.01.002]
点击复制

炉渣组分对CaO-Al2O3-SiO2-TiO2-MgO-Na2O渣系与铁液间硫分配比的影响(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2016年01期
页码:
5-10
栏目:
出版日期:
2016-02-29

文章信息/Info

Title:
Effect of composition on sulfur partition ratio between CaO-Al2O3-SiO2-TiO2-MgO-Na2O slags and hot iron
文章编号:
1674-9669(2016)01-0005-06
作者:
佟志芳1姜喜远1陈涛2
1.江西理工大学冶金与化学工程学院,江西,赣州 341000;
2. 湖南冶金职业技术学院冶金与材料系,湖南,株洲 412006
Author(s):
TONG Zhifang1 JIANG Xiyuan1 CHEN Tao2
1.School of Material and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhuo341000, China;
2. Department of Metallurgical and Material Engineering, Hunan Vocational College of Metallurgical Engineering, Zhuzhou 412006, China
关键词:
CaO-Al2O3-SiO2-TiO2-MgO-Na2O渣系硫分配比回归方程脱硫性能
分类号:
TF741.34
DOI:
10.13264/j.cnki.ysjskx.2016.01.002
文献标志码:
A
摘要:
针对高碱度高氧化铝的CaO-Al2O3-SiO2-TiO2-MgO-Na2O六元渣系,通过在1773K温度下测定其与铁液间的硫分配比研究了该渣系的脱硫性能。利用偏最小二乘法回归分析,建立了可很好预测硫分配比的回归方程,利用回归方程分析了炉渣碱度(mCaO/mSiO2), MgO, TiO2, Al2O3 以及 Na2O对硫分配比的影响。研究结果表明,当炉渣碱度大于2.9时,炉渣硫分配比均在140以上,表明该渣系具有较强的脱硫能力。在实验范围内,硫分配比随炉渣碱度的增加而提高。当碱度一定时,MgO对硫分配比的影响不大,TiO2 、Al2O3 均使硫分配比降低,其中Al2O3 降低硫分配比较为明显。硫分配比随Na2O增加而增加,少量的Na2O即可明显提高炉渣的脱硫能力。

参考文献/References:

[1] 张元福,刘永刚,甘国耀,等. 平果赤泥综合利用现状和开发研究展望[J].轻金属,2004(12):13-17.
[2] 毕诗文,杨毅宏,李殷泰,等.从铝酸钙炉渣中提铝的研究[J].轻金属,1992(6):10-15.
[3] Shankar A, Gornerup M, Lahiri A K, and Lahiri A. K. Sulfide capacity of high alumina blast furnace Slags[J]. Metall. Mater. Trans. B, 2006,37B:941.
[4]王竹民,吕庆,张淑会,等.邯钢高炉渣脱硫能力的试验研究[J]. 钢铁研究, 2008, 36(3)1-5.
[5]Dong K, Liu W L, Wen-juan and ZHU Rong. Desulfurization of CaO–Al2O3–SiO2–TiO2 Slag System [J]. ISIJ International, 2014, 54 (10): 2248–2254
[6] 郝 宁,王新华,刘金刚等.MgO含量对CaO-Al2O3-SiO2-MgO精炼渣脱硫能力的影响[J].炼钢,2009,25:416-419.
[7] CHOI Jayong, KIM Daejung and LEE Haegeon. Reaction Kinetics of Desulfurization of Molten Pig Iron Using CaO-Al2O3-SiO2–Na2O Slag Systems[J].ISIJ International, 2001,41 (3):216–224.
[8] 方开泰.均匀设计与均匀设计表[M].北京,科学出版社,1994,25-29.
[9]张志霞,胡长庆,魏航宇. 宣钢含钛高炉渣脱硫性能的实验研究[J].河北理工大学学报(自然科学版),2011,33(1):46-52.
[10]GuoHua ZHANG,, KuoChih CHOU, and Ken MILLS. Modelling Viscosities of CaO-Al2O3-SiO2-MgO Molten Slags [J]. ISIJ International, 2012,52(3):355-362.
[11] 张明博,李俊国,马红强.组分含量对CaO-MgO-Al2O3-SiO2四元精炼渣系粘度的影响[J].特殊钢,2013,34(2):28-31.
[12] REN Zhong-shan, HU Xiao-jun, CHOU Kuo-chih. Calculation and Analysis of Sulfide Capacities for CaO-Al2O3-SiO2-MgO-TiO2 Slags[J]. JOURNAL OF IRON AND STEEL RESEARCH. INTERNATIONAL,2013, 20(9):21-25.
[13] H. Kim, W. H. Kim, J. H. Park, and D. J. Min. A Study on the Effect of Na2O on the Viscosity for Ironmaking Slags [J]. Steel Research int. 2010, 81(1): 17-24.
[14]PAK J.J., ITO K. and FRUEHAN F.J. Activities of Na2O in CaO-based Slags Used for Dephosphorization of Steel [J]. ISI J International, 1989, 29 (4): 318-323.
[15]陆刚,成国光,宋波等.含BaO,Na2O渣系渣钢间硫平衡研究[J].包头钢铁学院学报,2001,20(3): 280-284.
[16]张典波,彭平.COREX法采用的高氧化镁渣性能及作用探讨[J].上海金属,1994,16(4): 23-27.

相似文献/References:

[1]佟志芳,姜喜远,陈涛.炉渣组分对CaO-Al2O3-SiO2-TiO2-MgO-Na2O渣系与铁液间硫分配比的影响[J].有色金属科学与工程,2015,(02):81.
 TONG Zhifang,JIANG Xiyuan,CHEN Tao.Effect of Composition on Sulfur Partition Ratio between CaO-Al2O3-SiO2-TiO2-MgO-Na2O slags and Hot Iron[J].,2015,(01):81.

备注/Memo

备注/Memo:
基金项目:国家自然科学基金资助项目(51174100)江西省自然科学基金资助项目(2010GZC0058)
作者简介:佟志芳(1972-),男,教授,主要从事冶金资源二次利用方面的研究,Email: tongzhifang1998@126.com
更新日期/Last Update: 2016-02-29