[1]杨少华,张丹城,田亚斌,等.5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究[J].有色金属科学与工程,2018,(02):1-5.[doi:10.13264/j.cnki.ysjskx.2018.02.001]
 YANG Shaohua,ZHANG Dancheng,TIAN Yabin,et al.Corrosion of 5083 aluminum magnesium alloy in NaClsolution with different concentrations[J].,2018,(02):1-5.[doi:10.13264/j.cnki.ysjskx.2018.02.001]
点击复制

5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2018年02期
页码:
1-5
栏目:
出版日期:
2018-05-21

文章信息/Info

Title:
Corrosion of 5083 aluminum magnesium alloy in NaClsolution with different concentrations
作者:
杨少华1张丹城12田亚斌1叶昌美1赵宇娟1李林山1
1.江西理工大学冶金与化学工程学院,江西 赣州 341000;2.中国科学院过程工程研究所,北京 100090
Author(s):
YANG Shaohua1 ZHANG Dancheng12 TIAN Yabin1 YE Changmei1 ZHAO Yujuan1 LI Linshan1
1.School of Metallurgical and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China; 2.Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100090, China
关键词:
5083铝镁合金扫描电化学显微镜极化曲线交流阻抗腐蚀
分类号:
TG172.3
DOI:
10.13264/j.cnki.ysjskx.2018.02.001
文献标志码:
A
摘要:
采用扫描电化学显微镜(SECM)中的极化曲线法和交流阻抗图谱法研究5083铝镁合金在不同浓度NaCl溶液中的腐蚀行为,结果表明:合金在中性NaCl溶液中的腐蚀为钝化材料体系,随着盐度的增加,Cl-对合金基体的破坏加剧,腐蚀电位正移,点蚀电位减小,其电化学阻抗谱中仅有1个容抗弧且呈现收缩趋势. 同时,阻抗减小,相位角增加,弥散指数降低,合金的耐腐蚀性能下降. 溶液中存在强活化作用的Cl-,会损坏合金表面的氧化膜,逐渐取代腐蚀产物Al(OH)3中的OH-,生成新的腐蚀产物AlCl3.

参考文献/References:

[1] 信绍广, 朱伟, 李军. 钢铁热喷涂金属涂层耐蚀性能的研究进展[J]. 金属世界, 2012(1):16-19.
[2] TOROS S, OZTURK F, KACAR I. Review of warm forming of aluminum–magnesium alloys[J]. Journal of Materials Processing Technology, 2008, 207(1/2/3):1-12.
[3] 杨少华,赵宇娟,李林山,等.微区电化学扫描技术应用现状[J].有色金属科学与工程,2017,8(3):29-34.
[4] 张艾艾, 何晶靖, 刘天娇,等. 5A06铝镁合金海水腐蚀电化学特性[J]. 航空学报, 2015, 36(9):3147-3154.
[5] 赵月红,林乐耘. 不同加工及表面处理状态LF6铝镁合金的深海腐蚀行为[J]. 中国有色金属学报, 2001, 11(增刊1):27-30.
[6] 穆振军, 陈翔峰, 任润桃,等. 45#钢和铝镁合金在淡海水交替环境下的腐蚀行为研究[C]// 2009’水环境腐蚀与防护学术研讨会,北京:中国腐蚀与防护学会水环境专业委员会, 2009.
[7] 王新印, 夏妍, 周亚茹,等. 基于扫描电化学显微镜产生/收集和反馈模式研究纯Mg腐蚀行为[J]. 金属学报, 2015, 51(5):631-640.
[8] TAN Y, LIU T. Characterising localised corrosion inhibition by means of parameters measured by an electrochemically integrated multielectrode array[J]. Corrosion Engineering Science & Technology, 2014, 49(1):23-31.
[9] 周亚茹, 朱泽洁, 聂林林,等. 氯离子浓度对Ni-P合金涂层失效过程影响的SECM实验和COMSOL模拟研究[J]. 表面技术, 2016, 45(7):8-16.
[10] 孙飞龙, 李晓刚, 卢琳,等. 5052和6061铝合金在中国南海深海环境下的腐蚀行为研究[J]. 金属学报, 2013, 49(10):1219-1226.
[11] 骆鸿,魏丹.金属腐蚀微区电化学研究进展(1)扫描电化学显微镜技术[J]. 腐蚀与防护,2009,30(7):437-441.
[12] KATEMANN B B, INCHAUPSE C G, CASTRO P A, et al. Precursor sites for localised corrosion on lacquered tinplates visualised by means of alternating current scanning electrochemical microscopy[J]. Electrochimica Acta, 2003, 48(9):1115-1121.
[13] SHI Y Y, ZHANG Z, SU J X, et al. EIS study on 2024-T3 aluminum alloy corrosion in simulated acid rain under cyclic wet-dry conditions[J]. Materials & Corrosion, 2005, 56(10):701-706.
[14] AHMAD S, GUPTA A P, SHARMIN E, et al. Synthesis, characterization and development of high performance siloxane- modified epoxy paints[J]. Prog Org Coat, 2005, 54: 248-255.
[15] SANCHEZ C M, SOLLA-GULLON J, VIDAL-IGLLESISA F J, et al. Imaging structure sensitive catalysis on different shape-controlled platinum nanoparticles[J]. Journal of the American Chemical Society, 2010, 132(16):5622-5625.
[16] 杨少华,刘增威,林明,等. 7075铝合金在不同pH值NaCl溶液中的腐蚀行为 [J]. 有色金属科学与工程 , 2017, 8(4): 26-30.
[17] MAZINANI S, S AMSAMI A , JAHANMIRI A, et al. Experimental study on equilibrium solubility (at low partial pressures), density, viscosity and corrosion rate of carbon dioxide in aqueous solutions of ascorbic acid[J]. Fuel & Energy Abstracts, 2011, 305(1):39-42.
[18] 吴茂永,田继强,曹立新,等.钨铝合金在不同NaCl溶液中的电化学腐蚀行为研究[J]. 腐蚀科学与防护技术,2015, 27(1):25-30.
[19] BURNS J T, G UPTA V K, A GNEW S R, et al. Effect of low temperature on fatigue crack formation and microstructure-scale propagation in legacy and modern Al-Zn-Mg-Cu alloys[J]. International Journal of Fatigue, 2013, 55(7):268-275.
[20] SOUTO R M, GONZALEZ-GARCIA Y, IZQUIERDO J, et al. Examination of organic coatings on metallic substrates by scanning electrochemical microscopy in feedback mode: revealing the early stages of coating breakdown in corrosive environments[J]. Corrosion Science, 2010, 52(3): 748-753.

相似文献/References:

[1]不同pH NaCl溶液中的腐蚀行为.基于SECM研究5083铝镁合金在[J].有色金属科学与工程,2018,(01预):31.
 YANG Shao hua,ZHANG Dan cheng,ZHAO Yujuan,et al.Study on corrosion behavior of 5083 aluminum magnesium alloy[J].,2018,(02):31.
[2]杨少华,张丹城,赵宇娟,等.基于SECM研究5083铝镁合金在不同pH NaCl溶液中的腐蚀行为[J].有色金属科学与工程,2018,(01):22.[doi:10.13264/j.cnki.ysjskx.2018.01.004]
 YANG Shaohua,ZHANG Dancheng,ZHAO Yujuan,et al.A study on the corrosion behavior of 5083 aluminum magnesium alloy in the NaCl solutions of different pH by SECM[J].,2018,(02):22.[doi:10.13264/j.cnki.ysjskx.2018.01.004]
[3]杨少华,张丹城,赵宇娟,等.5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究[J].有色金属科学与工程,2018,(02预):51.
 YANG Shaohua,ZHANG Dancheng,ZHAO Yujuan,et al.Corrosion of 5083 Aluminum Magnesium Alloy in NaCl[J].,2018,(02):51.

备注/Memo

备注/Memo:
收稿日期:2017-09-20
基金项目:国家自然科学基金资助项目(51664022)
通信作者:杨少华(1975- ), 男,博士,副教授,主要从事熔盐电解和合金腐蚀方面的研究,E-mail: xizi527@163.com.
更新日期/Last Update: 2018-04-20