[1]叶昌美,陈功,韦茗仁,等.NaCl-KCl-NaF-WO3熔盐体系W6+的电化学行为[J].有色金属科学与工程,2019,(01):20-27.[doi:10.13264/j.cnki.ysjskx.2019.01.004]
 YE Changmei,CHEN Gong,WEI Mingren,et al.Electrochemical behavior of W6+ in NaCl-KCl-NaF-WO3 molten salt system[J].,2019,(01):20-27.[doi:10.13264/j.cnki.ysjskx.2019.01.004]
点击复制

NaCl-KCl-NaF-WO3熔盐体系W6+的电化学行为(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2019年01期
页码:
20-27
栏目:
出版日期:
2019-01-20

文章信息/Info

Title:
Electrochemical behavior of W6+ in NaCl-KCl-NaF-WO3 molten salt system
作者:
叶昌美1 陈功1 韦茗仁2 田亚斌1 黄晶晶1 王昭文1 杨少华1
(1.江西理工大学冶金与化学工程学院, 江西 赣州 341000; 2.中南大学冶金与环境工程学院,长沙 410006)
Author(s):
YE Changmei1 CHEN Gong1 WEI Mingren2 TIAN Yabin1 HUANG Jingjing1 WANG Zhaowen1YANG Shaohua1
(1. School of Metallurgical and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China; 2. School of Metallurgy and Environment, Central South University, Changsha 410006, China)
关键词:
NaCl-KCl-NaF-WO3熔盐电化学行为扩散系数
分类号:
TF841.1
DOI:
10.13264/j.cnki.ysjskx.2019.01.004
文献标志码:
A
摘要:
实验以NaCl-KCl-NaF为电解质体系,WO3为原料,利用循环伏安法、计时电位法、计时电流法和方波伏安法,研究温度为973 K时钨离子在钨电极上的电化学过程. 结果表明:W(VI)离子的还原过程分2步进行,第1步还原过程为两电子转移,电极反应方程式为W6++2e-→W4+;第2步还原过程为四电子转移过程,电极反应方程式为W4++4e-→W,且都为准可逆反应. W(VI)离子在钨电极上的还原过程受扩散控制,扩散系数为1.05×10-9 cm2/s.

参考文献/References:


[1] 冯乃祥, 刘希诚, 孙阳. 用熔盐电解法制备超细钨粉[J]. 材料研究学报, 2001, 15(4): 459-462.
[2] 冯乃祥,孙阳, 葛贵军. NaCl-Na2WO4-WO3 系熔盐电解法制备超细钨粉的研究[J]. 稀有金属, 2001, 25(5): 374-377.
[3] NAKAJIMA H, NOHIRA T, HAGIWARA R, et al. Electrodeposition of metallic tungsten films in ZnCl2-NaCl-KCl-KF-WO3 melt at 250 °C[J]. Electrochimica Acta, 2007, 53(1): 24-27.
[4] NITTA K, NOHIRA T, HAGIWARA R, et al. Electrodeposition of tungsten from ZnCl2-NaCl-KCl-KF-WO3 melt and investigation on tungsten species in the melt[J]. Electrochimica Acta, 2010, 55(3):1278-1281.
[5] 廖春发, 杨文强, 王旭,等. 由钨酸盐熔盐电解直接制备钨粉的可行性分析[J]. 有色金属科学与工程, 2011, 2(4):4-6.
[6] 王旭, 廖春发, 杨文强,等. CaWO4-NaCl-CaCl2体系熔盐电解制备钨粉的表征与电化学分析[J]. 中国有色金属学报, 2012, 22(5): 1482-1487.
[7] 王旭, 廖春发, 汪浩. NaCl-CaCl2-Na2WO4体系电解制备钨粉过程表征[J]. 北京工业大学学报, 2012, 38(6): 938-941.
[8] SUN N B, ZHANG Y C, JIANG F, et al. Preparation of tungsten coatings on graphite by electro-deposition via Na2WO4-WO3 molten salt system[J]. Fusion Engineering and Design, 2014, 89(11): 2529-2533.
[9] FAN J, ZHANG Y, SUN N, et al. Effect of direct current density on microstructure of tungsten coating electroplated from Na2WO4-WO3-NaPO3 system[J]. Applied Surface Science, 2014, 317: 867-874.
[10] JIANG F, ZHANG Y, SUN N, et al. Effect of pulse current parameters on microstructure of tungsten coating electroplated from Na2WO4-WO3-NaPO3[J]. Applied Surface Science, 2015, 331: 278-284.
[11] 张明杰,王兆文. 熔盐电化学原理与应用[M].北京:化学工业出版社,2006,9(1): 231-238.
[12] 王川,陈晓明,何佩鑫,等. 可逆、准可逆和不可逆表面反应循环伏安法的数字模拟[J]. 高等学校化学学报,1991,7 (12):875-878.
[13] BARD A J, FAULKNER L R. Electrochemical fundamentalsand applications (2nd Edition)[M]. New York: John Wiley and Sons INC, 2003: 225- 227.
[14] LI M, SUN T T, LIU B, et al. Elec-trochemical behavior of Dy(Ⅲ) and the selective formation of Dy-Ni intermetallic compounds in LiCl-KCl eutectic melts[J]. Acta Physico-Chimica Sinica, 2015, 31(2):309-314.
[15] PAUL M S MONCK. Fundamentals of electroanalytical chemistry[M]. Beijing: Chemical Industry Press, 2001: 100-101.
[16] 王岗. 超细钨粉及碳化钨粉制备工艺研究[D]. 上海:上海交通大学,2009.
[17] MACDONALD D D. Transient techniques in electrochemistry[M]. New York: Plenum Press, 1979.

相似文献/References:

[1]王林生.轻稀土元素共电积试验研究[J].有色金属科学与工程,1999,(04):18.
[2]廖春发,房孟钊,王旭,等.NaCl-KCl-Na2WO4共融体系的方波伏安法分析[J].有色金属科学与工程,2015,(04):6.[doi:10.13264/j.cnki.ysjskx.2015.04.002]
 LIAO Chunfa,FANG Mengzhao,WANG Xu,et al.Square wave voltammetry analysis of NaCl-KCl-Na2WO4 communion system[J].,2015,(01):6.[doi:10.13264/j.cnki.ysjskx.2015.04.002]
[3]杨凤丽,王浩然,谢宝如,等.钨酸根离子在银、金电极上的电化学行为研究[J].有色金属科学与工程,2016,(05预):235.
 Yang Fengli,Wang Haoran,Xie Baoru,et al.Electrochemical behavior of tungstate ion on gold, silver electrode[J].,2016,(01):235.
[4]杨凤丽,王浩然,谢宝如,等.钨酸根离子在银、金电极上的电化学行为研究[J].有色金属科学与工程,2016,(04):9.[doi:10.13264/j.cnki.ysjskx.2016.04.002]
 YANG Fengli,WANG Haoran,XIE Baoru,et al.Electrochemical behavior of tungstate ion on gold and silver electrode[J].,2016,(01):9.[doi:10.13264/j.cnki.ysjskx.2016.04.002]
[5]叶昌美,韦茗仁,田亚斌,等.NaCl-KCl-NaF-WO3熔盐体系W6+的电化学行为[J].有色金属科学与工程,2019,(01):13.
 YE Changmei,WEI Mingren,TIAN Yabing,et al.Electrochemical behavior of W6+ in NaCl-KCl-NaF-WO3 molten salt system[J].,2019,(01):13.

备注/Memo

备注/Memo:
收稿日期:2018-10-22
基金项目:国家自然科学基金资助项目(51664022);江西省教育厅青年科学基金资助项目(GJJ170544);江西理工大学博士启动基金资助项目(jxxjbs16002)
通信作者:陈功(1984- ),男,博士,讲师,主要从事熔盐电化学,铝电解应用基础方面的研究,E-mail:chengong_mse@163.com.
更新日期/Last Update: 2019-02-20