[1]黄国杰,洪松柏,郑国辉,等.C17510弹性合金的固溶时效与组织性能的研究[J].有色金属科学与工程,2014,(05):45-48,73.[doi:10.13264/j.cnki.ysjskx.2014.05.008]
 HUANG Guojie,HONG Songbai,ZHENG Guohui,et al.Effects of solid solution and aging treatment on the microstructure and properties of elastic C17510 alloy[J].,2014,(05):45-48,73.[doi:10.13264/j.cnki.ysjskx.2014.05.008]
点击复制

C17510弹性合金的固溶时效与组织性能的研究(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2014年05期
页码:
45-48,73
栏目:
冶金·材料
出版日期:
2014-10-20

文章信息/Info

Title:
Effects of solid solution and aging treatment on the microstructure and properties of elastic C17510 alloy
作者:
黄国杰1洪松柏2郑国辉2赵洋1汪东亚3彭丽军1
1.北京有色金属研究总院有色金属材料制备加工国家重点实验室,北京100088;2.鹰潭兴业电子金属材料有 限公司,江西鹰潭335000; 3.宁波兴业盛泰集团有限公司,浙江宁波315336
Author(s):
HUANG Guojie1 HONG Songbai2 ZHENG Guohui2 ZHAO Yang1 WANG Dongya3 PENG Lijun1
1.General Research Institute for Nonferrous Metals, State key laboratory of Nonferrous Metals, Beijing 100088,China; 2. Yintan Shine Electric Metal Material Co. Ltd, Yintan 335000,China; 3. NingBo Xingye ShengTai Group Co. Ltd, Ningbo 315336,China
关键词:
C17510合金固溶时效处理微观组织维氏硬度电导率
分类号:
TG146.11;TF125.2
DOI:
10.13264/j.cnki.ysjskx.2014.05.008
文献标志码:
A
摘要:
采用OM、SEM、XRD和TEM分析手段对C17510合金的固溶时效与组织性能进行研究.结果表明,冷轧态 C17510合金的合理固溶处理温度为950℃.时效态C17510合金的硬度与时间呈单峰型曲线,合金的电导率与时 间呈先剧增,后缓慢增大,最后趋于稳定的趋势.冷轧态C17510合金经950℃×0.5h固溶处理+525℃×4h时 效处理后,其维氏硬度为231,电导率为56%IACS.

参考文献/References:

[1] 陈乐平, 周全. 铍铜合金的研究进展及应用[J]. 材料热处理技术, 2009, 38(22): 14-18.
[2] 潘奇汉. 铍铜合金性能与其元件生产[J]. 电子元件与材料, 2004, 23(2): 44-45.
[3] 董超群, 易均平. 铍铜合金市场与应用前景展望[J]. 稀有金属, 2005, 29(3): 350-356.
[4] 阎永, 汪治军, 董超群. 我国铍铜产业科技进步回顾与展望[J]. 稀有金属,2003, 27(1): 66-68.
[5] 刘楚明, 刘娜, 曾祥亮, 等. 形变时效工艺对低铍Cu-Ni-Be 合金力学性能和电导率的影响[J]. 中南大学 学报(自然科学版),2010, 41(2): 508-513.
[6] Bonfield W, Edwardsb C. Precipitation hardening in Cu-1.8wt%Be-0.28wt%Co[J]. Journal of Material Science, 1974, 9(3): 398-408.
[7] Masamichi M, Yoshikiyo O. Effect of Quenching temperature on the intragranular and cellular precipitations in Cu-1.5%Be Binary alloy[J]. Material Transactions, JIM, 1995, 36(9): 1118-1123.
[8] Donoso E, Varschavsky A. Microcalorimetric evaluation of precipitation in Cu-2Be-0.2Mg[J]. Journal of Thermal Analysis and Calorimetry, 2001,63(1): 249-266.
[9] Chihiro W, Toshiro S, Ryoichi M. Misfit strains of precipitations phase and dimensional changes in Cu-Be alloys[J]. Philosophical Magazine, 2008, 88(9): 1401-1410.
[10] Ryoichi M, Tsutomu S, Toshiro S, et al. Precipitation processes in Cu-0.9mass%Be single Crystal[J]. Material Transactions, JIM, 2006,47(12): 2925-2934.
[11] Peng L J, Xiong B Q, Xie G L, et al. Precipitation process and its effects on properties of aging Cu-Ni-Be alloy[J]. Rare Metals, 2013, 32(4): 332-337.
[12] Rioja R J, Laughlin D E. The sequence of precipitation in Cu-2wt%Be Alloys[J]. Acta Metallurgica, 1980, 28(8): 1301-1313.
[13] Chihiro W, Ryoichi M. Precipitation process in a Cu-Ni-Be alloy[J].Solid State Phenomena, 2011, 172/173/174: 432-426.
[14] Satoshi O, Naokuni M, Kazumasa S, et al. Mechanical and Electrical proprieties and microstructure in Cu-Ni-Be alloys[J]. Journal of the Society of Material Science, 2007, 56(6): 531-536.
[15] Guha A. Development of a high strength high conductivity Cu-Ni-Be alloy[J]. High Conductivity copper and Aluminum Alloys, 1984, 26: 133-145.

相似文献/References:

[1]黄国杰,洪松柏,郑国辉,等.C17510弹性合金的固溶时效与组织性能的研究[J].有色金属科学与工程,2015,(02预):20.

备注/Memo

备注/Memo:
收稿日期:2014-10-08 基金项目:北京市科技项目(10231103);科研院所技术开发研究专项基金(2011DIA5k023) 作者简介:黄国杰(1979- ),男,博士,教授,主要从事先进铜合金材料的制备与加工研究,E-mail: huangguojie@grinm.com.
更新日期/Last Update: 2014-10-20