[1]不同pH NaCl溶液中的腐蚀行为.基于SECM研究5083铝镁合金在[J].有色金属科学与工程,2018,(01预):31-35.
 YANG Shao hua,ZHANG Dan cheng,ZHAO Yujuan,et al.Study on corrosion behavior of 5083 aluminum magnesium alloy[J].,2018,(01预):31-35.
点击复制

基于SECM研究5083铝镁合金在(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2018年01期预
页码:
31-35
栏目:
出版日期:
2018-01-20

文章信息/Info

Title:
Study on corrosion behavior of 5083 aluminum magnesium alloy
作者:
不同pH NaCl溶液中的腐蚀行为
江西理工大学冶金与化学工程学院,江西赣州,341000;2.中国科学院过程工程研究所,北京,100090 )
Author(s):
YANG Shao hua1ZHANG Dan cheng2 ZHAO Yujuan1 LI Linshan1
(1.College of Metallurgical and Chemical Engineering, Jiangxi University of Science and Technology, Ganzhou 341000 , China; 2.Institute of process engineering, Chinese Academy of Sciences, Beijing, 100090,China)
关键词:
5083铝镁合金扫描电化学显微镜极化曲线电化学阻抗图谱腐蚀
分类号:
TG172.3
DOI:
-
文献标志码:
A
摘要:
采用扫描电化学显微镜(SECM)中的极化曲线法和交流阻抗图谱法研究5083铝镁合金在不同pH NaCl溶液中的腐蚀行为,结果表明:在酸性体系(pH 3~7),随着pH的增加,其腐蚀电位正移,点蚀电位相差不大,维钝电流密度减小,电化学阻抗谱中仅有1个容抗弧且呈现收缩趋势。同时,阻抗和相位角减小,电荷传递电阻升高,耐腐蚀性能增大。在碱性体系(pH 9~12),随着pH的增加,腐蚀电流密度增加,而腐蚀电位减小,腐蚀速度由0.0009mm/a增加到0.0256?mm/a。电化学阻抗谱中有2个容抗弧,在pH=12处出现感抗弧。同时,阻抗和相位角减小,金属化合物颗粒溶解过程加快,合金耐腐蚀性能降低。

参考文献/References:

[1]杨渊, 李玉光, 涂树林. 国外热镀锌铝镁合金镀层钢板及其标准综述[J]. 冶金标准化与质量, 2013(6):45-49.
[2]祝晓文, 韩建民, 崔世海,等. 铝、镁合金微弧氧化技术研究进展[J]. 材料科学与工艺, 2006, 14(4):366-369.
[3]张静, 潘复生, 李忠盛. 耐热镁合金材料的研究和应用现状[J]. 铸造, 2004, 53(10):770-774.
[4]张艾艾, 何晶靖, 刘天娇,等. 5A06铝镁合金海水腐蚀电化学特性[J]. 航空学报, 2015, 36(9):3147-3154.
[5]赵月红,林乐耘. 不同加工及表面处理状态LF6铝镁合金的深海腐蚀行为[[J]. 中国有色金属学报, 2001, 11(s1):27-30.
[6]穆振军, 陈翔峰, 任润桃,等. 45#钢和铝镁合金在淡海水交替环境下的腐蚀行为研究[C]// 2009’水环境腐蚀与防护学术研讨会. 2009.
[7]王新印, 夏妍, 周亚茹,等. 基于扫描电化学显微镜产生/收集和反馈模式研究纯Mg腐蚀行为[J]. 金属学报, 2015, 51(5):631-640.
[8]Michael V Mirkin ,Benjamin R Horrocks. Elect roanalytical measurements using the scanning elect rochemical microscope [ J ] . Analytica Chimica Acta , 2000(406) :119 - 146.
[9]周亚茹, 朱泽洁, 聂林林,等. 氯离子浓度对Ni-P合金涂层失效过程影响的SECM实验和COMSOL模拟研究[J]. 表面技术, 2016, 45(7):8-16.
[10]杨少华,赵宇娟,李林山,等.微区电化学扫描技术应用现状[J].有色金属科学与工程, 2017(03):29-34.
[11]骆鸿,魏丹.金属腐蚀微区电化学研究进展(1)扫描电化学显微镜技术[J],腐蚀与防护, 2009, 30(7):437-441.
[12]Bernardo Ballesteros Katemann ,Carlota González Inchauspe. Precursor sites for localised corrosion on lacquered tinplates visualised by means of alternating current scanning electrochemical microscop y [ J ] .Electrochimica Acta ,2003 (48) :1151 - 1121.
[13]Li J G, Wu Z S. Anti-corrosive Surface Engineering and Technology [M]. Beijing: Chemical Industry Press, 2003: 2, 54(李金桂, 吴再思. 防腐蚀表面工程技术 [M]. 北京: 化学工业出版社, 2003: 2, 54)..
[14]Ahmad S, Gupta A P, Sharmin E, et al. Synthesis, characterization and development of high performance siloxane- modified epoxy paints [J]. Prog. Org. Coat., 2005, 54: 248-255.
[15]SANCHEZ-SANCHEZ C M, SOLLA-GULLON J, VIDAL-IGLESIAS F J, et al. Imaging structure sensitive catalysis on different shape-controlled platinum nanoparticles[J]. Journal of the American Chemical Society, 2010, 132(16): 5622-5624.
[16]HENDERSON J D, FILICE F P, Li M S, et al. Tracking live cell response to cadmium (II) concentrations by scanning electrochemical microscopy.[J]. Journal of Inorganic Biochemistry, 2015, 158:92-98.

相似文献/References:

[1]杨少华,张丹城,赵宇娟,等.基于SECM研究5083铝镁合金在不同pH NaCl溶液中的腐蚀行为[J].有色金属科学与工程,2018,(01):22.[doi:10.13264/j.cnki.ysjskx.2018.01.004]
 YANG Shaohua,ZHANG Dancheng,ZHAO Yujuan,et al.A study on the corrosion behavior of 5083 aluminum magnesium alloy in the NaCl solutions of different pH by SECM[J].,2018,(01预):22.[doi:10.13264/j.cnki.ysjskx.2018.01.004]
[2]杨少华,张丹城,赵宇娟,等.5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究[J].有色金属科学与工程,2018,(02预):51.
 YANG Shaohua,ZHANG Dancheng,ZHAO Yujuan,et al.Corrosion of 5083 Aluminum Magnesium Alloy in NaCl[J].,2018,(01预):51.
[3]杨少华,张丹城,田亚斌,等.5083铝镁合金在不同浓度NaCl溶液中的腐蚀研究[J].有色金属科学与工程,2018,(02):1.[doi:10.13264/j.cnki.ysjskx.2018.02.001]
 YANG Shaohua,ZHANG Dancheng,TIAN Yabin,et al.Corrosion of 5083 aluminum magnesium alloy in NaClsolution with different concentrations[J].,2018,(01预):1.[doi:10.13264/j.cnki.ysjskx.2018.02.001]

备注/Memo

备注/Memo:
收稿日期:基金项目:国家自然科学基金资助项目(51664022)
更新日期/Last Update: 2017-11-17