[1]邱世涛a,b,钟盛文a,等.Cu掺杂LiNi0.6Co0.2Mn0.2O2的电化学性能[J].有色金属科学与工程,2018,(05):26-32.[doi:10.13264/j.cnki.ysjskx.2018.05.005]
 QIU Shitaoa,b,ZHONG Shengwena,et al.Study on electrochemical performance of Cu-added LiNi0.6Co0.2Mn0.2O2[J].,2018,(05):26-32.[doi:10.13264/j.cnki.ysjskx.2018.05.005]
点击复制

Cu掺杂LiNi0.6Co0.2Mn0.2O2的电化学性能(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2018年05期
页码:
26-32
栏目:
出版日期:
2018-09-30

文章信息/Info

Title:
Study on electrochemical performance of Cu-added LiNi0.6Co0.2Mn0.2O2
作者:
邱世涛ab 钟盛文ab李婷婷ab杨金猛ab田丰ab
江西理工大学,a.材料科学与工程学院;b.江西省动力电池及其材料重点实验室,江西 赣州 341000
Author(s):
QIU ShitaoabZHONG ShengwenabLI TingtingabYANG JinmengabTIAN Fengab
a. School of Materials Science and Engineering; b. Jiangxi Key Laboratory of Power Battery and Materials,Jiangxi University of Science and Technology,Ganzhou 341000,China
关键词:
铜掺杂LiNi0.6Co0.2Mn0.2O2锂离子电池电化学性能
分类号:
-
DOI:
10.13264/j.cnki.ysjskx.2018.05.005
文献标志码:
-
摘要:
采用共沉淀法制备前驱体,高温固相合成正极材料Li(Ni0.6Co0.2Mn0.2)1-xCuxO2(x=0、0.01、0.015和0.02),通过X射线衍射、SEM和电池测试系统及电化学工作站测试,对其结构 、形貌和电化学性能进行表征.结果表明,掺杂少量的Cu, 样品均具有α-NaFeO2型结构,没有出现杂相;样品(108)/(110)峰分裂明显,材料有着良好的层状结构;随着Cu掺杂量的增加,c和c/a增大,层间距增大,Li+脱嵌通道增大,改善导电性.Cu掺杂1 %和1.5 % 的I(003)/I(104)比值分别为1.467、1.438,比0%的1.431值大,减小了阳离子混排.首次放电比容量依次为170.6 mAh/g、164.1 mAh/g、163.6 mAh/g和162.4 mAh/g,当x为0,1 %,2 %经过100次循环,保持率为87.1 %、98.7 %、和87.7 %; x为1.5 %,比容量从161.8 mAh/g增加到173.9 mAh/g,性能较优.

参考文献/References:


[1]徐悦斌, 钟胜奎, 张倩. Ti掺杂LiNi0.6Co0.2Mn0.2O2的制备及电化学性能[C]// 中国功能材料及其应用学术会议. 2010.
[2]张芸. 锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2的合成及其电化学性能研究[D].南京: 南京工业大学, 2016.
[3]袁晶. 锂离子电池正极材料LiNi0.6Co0.2Mn0.2O2的合成与改性[D].合肥: 合肥工业大学, 2017.
[4]吕庆文. 高容量镍基正极材料LiNi0.9Mn0.1O2的合成及改性研究[D]. 赣州:江西理工大学, 2017.
[5]卢道焕, 胡明超, 黄瑞鸿,等. 锂离子电池材料LiNi0.6Co0.2Mn0.2O2的制备与性能研究[J]. 中国锰业, 2017(增刊1):47-50.
[6]吕庆文, 尹从岭, 钟盛文,等. LiNi0.6Co0.1Mn0.3O2正极材料的合成与性能[J]. 有色金属科学与工程, 2016, 7(4):50-54.
[7]李龙. 锂离子电池镍钴锰三元正极材料的合成与改性研究[D]. 北京:清华大学, 2012.
[8]PENG Y, WANG Z, PENG W, et al. Spray-drying synthesized LiNi0.6Co0.2Mn0.2O2 and its electrochemical performance as cathode materials for lithium ion batteries[J]. Powder Technology, 2011, 214(3):279-282.
[9]Cheng K L, Mu D B, Wu B R, et al. Electrochemical performance of a nickel-rich LiNi0.6Co0.2Mn0.2O2 cathode material for lithium-ion batteries under different cut-off voltages[J]. International Journal of Minerals Metallurgy and Materials, 2017, 24(3):342-351.
[10]YUAN J, WEN J, ZHANG J, et al. Influence of calcination atmosphere on structure and electrochemical behavior of LiNi0.6Co0.2Mn0.2O2, cathode material for lithium-ion batteries[J]. Electrochimica Acta, 2017, 230:116-122.
[11]LEI W,MU D B,WU B R,et al. Enhanced electrochemical performance of Lithium Metasilicate-coated LiNi0.6Co0.2Mn0.2O2, Ni-rich cathode for Li-ion batteries at high cutoff voltage[J]. Electrochimica Acta, 2016, 222:806-813.
[12]陈亮, 唐新村, 张阳,等. 从废旧锂离子电池中分离回收钴镍锰[J]. 中国有色金属学报, 2011, 21(5):1192-1198.
[13]陈亮. 废旧锂离子电池中有色金属资源化回收利用研究[D].长沙: 中南大学, 2011.
[14]王东, 吴照金. Cu掺杂对锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3] O2的影响[J]. 当代化工, 2015(10):2335-2337.
[15]HUANG Y, WANG Z X, LI X H, et al. Synthesis of Ni0.8Co0.1Mn0.1(OH)2, precursor and electrochemical performance of LiNi0.8Co0.1Mn0.1O2, cathode material for lithium batteries[J]. Transactions of Nonferrous Metals Society of China, 2015, 25(7):2253-2259.
[16]CHEN Y, ZHANG Y, CHEN B, et al. An approach to application for LiNi0.6Co0.2Mn0.2O2, cathode material at high cutoff voltage by TiO2, coating[J]. Journal of Power Sources, 2014, 256(12):20-27.
[17]赖江洪, 钟盛文, 郭进康,等. LiNi1/3Co1/3Mn1/3O2正极材料的合成与性能[J]. 有色金属科学与工程, 2017, 8(4):68-72.
[18]陆雷, 钟伟攀, 杨晖. 高致密球形LiNi0.8Co0.1Mn0.1O2颗粒的合成及性能研究[J]. 无机材料学报, 2012, 27(3):258-264.
[19]郑卓, 吴振国, 向伟,等. Na+掺杂锂离子电池正极材料 LiNi0.6Co0.2Mn0.2O2的制备及电化学性能[J]. 高等学校化学学报, 2017, 38(8):1458-1464.
[20]YUAN J, WEN J, ZHANG J, et al. Influence of calcination atmosphere on structure and electrochemical behavior of LiNi0.6Co0.2Mn0.2O2, cathode material for lithium-ion batteries[J]. Electrochimica Acta, 2017, 230:116-122.
[21]夏云飞. 层状三元材料LiNi0.6Co0.2Mn0.2O2的烧结工艺及其Al离子掺杂改性研究[D]. 哈尔滨:哈尔滨工业大学, 2015.
[22]郝晶敏, 刘海萍, 吉元鹏,等. 锡掺杂LiNi0.5Mn1.5O4锂离子电池高电压正极材料的制备及性能研究(英文)[J]. Science China.Materials, 2017(4):315-323.

相似文献/References:

[1]邱世涛a,b,钟盛文a,等.Cu掺杂LiNi0.6Co0.2Mn0.2O2的电化学性能[J].有色金属科学与工程,2018,(05预):10.
 QIU Shitaoa,bZHONG Shengwena,bLI Tingtinga,et al..2O2[J].,2018,(05):10.

备注/Memo

备注/Memo:
收稿日期:2018-07-13
基金项目:江西省科技计划资助项目(20151BBE50106)
通信作者:钟盛文(1963-)男,教授,博导,主要从事锂离子电池正极材料方面的研究,E-mail: zhongshw@126.com.
更新日期/Last Update: 2018-09-30