[1]韩秀秀,张廷安,吕国志,等.电转化和氢氧化钠滴定法从氯化铝溶液中制备氧化铝及其性能对比研究[J].有色金属科学与工程,2019,(04):16-21.[doi:10.13264/j.cnki.ysjskx.2019.04.003]
 HAN Xiuxiu,ZHANG Tingan,LYU Guozhi,et al.A comparative study of alumina prepared from aluminum chloride solution by electrotransformation method and by sodium hydroxide titration method[J].,2019,(04):16-21.[doi:10.13264/j.cnki.ysjskx.2019.04.003]
点击复制

电转化和氢氧化钠滴定法从氯化铝溶液中制备氧化铝及其性能对比研究(/HTML)
分享到:

《有色金属科学与工程》[ISSN:1674-9669/CN:36-1311/TF]

卷:
期数:
2019年04期
页码:
16-21
栏目:
出版日期:
2019-07-20

文章信息/Info

Title:
A comparative study of alumina prepared from aluminum chloride solution by electrotransformation method and by sodium hydroxide titration method
文章编号:
1674-9669(2019)04-0016-06
作者:
韩秀秀 张廷安 吕国志 潘喜娟
(东北大学,多金属共生矿生态化冶金教育部重点实验室,沈阳110819)
Author(s):
HAN Xiuxiu ZHANG Tingan LYU Guozhi PAN Xijuan
(Key Laboratory for Ecological Metallurgy of Multimetallic Mineral (Ministry of Education), Northeastern University, Shenyang 110819, China)
关键词:
氧化铝氯化铝溶液电转化法氢氧化钠滴定法
分类号:
TF821
DOI:
10.13264/j.cnki.ysjskx.2019.04.003
文献标志码:
A
摘要:
目前,我国存在许多以氯化铝溶液为原料制备氧化铝的方法. 然而,这些方法均存在着许多不足之处,如产生废酸和废盐、制备条件要求较高、反应中涉及有毒有害物质等. 基于这种情况,在氯碱工业的启发下,东北大学已经提出了一种电转化AlCl3水溶液制备氧化铝的新方法. 并且该方法已经得到了试验性验证. 文中主要研究了电转化新方法和氢氧化钠滴定法制备的氧化铝前驱体在红外光谱及粒度分布方面的不同;同时研究了这2种方法制备的氧化铝在物相、形貌及粒度等方面的差异. 结果表明,这2种方法制备的氧化铝前躯体均含有铝元素及Al-OH键,且其焙烧产物也均为氧化铝. 与氢氧化钠滴定法制备的氧化铝相比,电转化法制备的氧化铝形貌较规整且为片状结构,而氢氧化钠滴定法制备的氧化铝形状不规则. 同时,电转化法制备的氧化铝及其前驱体的粒径小于氢氧化钠滴定法制备的氧化铝及其前躯体的粒径,但前者的粒径分布比后者的粒径分布更为均匀.

参考文献/References:

[1] 樊青枝. 我国氧化铝工业的生产现状及发展战略[J]. 山西财经大学学报, 2000, 22(4):38-39.
[2] 商连弟, 武换荣, 张艳红. 中国化学品氧化铝生产现状及发展趋势[J]. 无机盐工业, 2009, 41(12):11-13.
[3] 陆钦芳. 我国氧化铝工业的现状及发展对策[C]//沈阳:沈阳铝镁设计院,中国有色金属学会学术会议. 1997.
[4] 王彧. 我国氧化铝市场现状及发展方向[J]. 中国高新技术企业, 2012(14):10-11.
[5] 祖树正. 铝土矿资源合理开发利用的探讨[J]. 江西有色金属, 1999, 13(2):12-14.
[6] 陶英君, 杨玉华. 我国氧化铝工业现状与发展建议——第三次全国工业普查资料分析[J]. 轻金属, 1998(7):3-9.
[7] 朱妍, 霍云波. 2015年氧化铝市场回顾及展望[J]. 中国有色金属,2016(7):50-51.
[8] 车玲. 我国氧化铝工业技术现状与发展趋势[J]. 世界有色金属, 2005(5):14-18.
[9] WU X, MENG X, DING J, et al. Preparation of core-shell structured amorphous aluminum hydroxide ultra-fine powders via a microwave-hydrothermal route[J]. Materials Letters, 2011, 65(14): 2133-2135.
[10] 江琦, 雷蕾. 醇盐水解-水热法制备高结晶度纳米氢氧化铝[J]. 材料导报: 纳米与新材料专辑, 2008(3): 23-25.
[11] LEE J S, KIM H S, PARK N K, et al. Low temperature synthesis of α -alumina from aluminum hydroxide hydrothermally synthesized using [Al(C2O4)x(OH)y] complexes[J]. Chemical Engineering Journal, 2013, 230: 351-360.
[12] PANASYUK G P, AZAROVA L A, VOROSHILOV I L, et al. Preparation of nanocrystalline aluminum hydroxide and alumina by thermal and vapor heat treatments of reaction products of terephthalic acid and aluminum hydroxide[J]. Inorganic Materials, 2011, 47(3): 273-278.
[13] KINOSHITA K, MINAMI H, TARUTANI Y, et al. Preparation of aluminum hydroxide and alumina particles in an ionic liquid[J]. Chemistry Letters, 2010, 39(7): 741-743.
[14] KINOSHITA K, MINAMI H, TARUTANI Y, et al. Preparations of polystyrene/aluminum hydroxide and polystyrene/alumina composite particles in an ionic liquid[J]. Langmuir, 2011,27(8): 4474-4480.
[15] JANG C R, HAN K B, VOICU V, et al. Impregnation of catalytic active components in an ammonia solution during granulation of aluminium hydroxide gel by sol-gel method in hydrocarbon-ammonia moulding column[J]. Revista De Chimie, 2012, 63(12): 1301-1305.
[16] FARAG H K, Al ZOUBI M, ENDRES F. Sol-gel synthesis of alumina, titania and mixed alumina/titania in the ionic liquid1-butyl-1-methylpyrrolidinium bis (trifluoromethylsulphonyl) amide[J]. Journal of Materials Science, 2009, 44 (1):122-128.
[17] 王莉, 张丽云. 水热法制备氢氧化铝晶须研究[J]. 科学技术与工程, 2011, 11(24): 5906-5909.
[18] 王凌云, 童东绅, 祝军兵, 等. 氢氧化铝的制备方法及应用[J]. 浙江化工, 2014(12):24-29.
[19] CASTRUITA G, ERERA-MERCADO Y A, SAUCEDO-SALAZAR E M, et al. Sol-gel aluminum hydroxides and their thermal transformation studies for the production of alpha-alumina[J]. Journal of Inorganic and Organometallic Polymers and Materials, 2013, 23(5): 1145-1152.
[20] SUZUKI T, TAMAGAWA S. Aluminum hydroxide gel particle and production method thereof: US, 13/759 447[P]. 2013-02-05.
[21] ZHANG Y, ZHANG T A, DREISINGER D, et al. Chelating extraction of vanadium(V) from low pH sulfuric acid solution by Mextral 973H[J]. Separation and Purification Technology, 2018, 190:123-135.

相似文献/References:

[1]秦国红.中州分公司烧结法氧化铝生产脱硅工艺的发展[J].有色金属科学与工程,2010,(3/4):0.
 QIN Guo-hong.On the Development of Alumina’s Sintered Silicon Technology of a Company[J].,2010,(04):0.
[2]韩秀秀,张廷安,吕国志,等.电转化和氢氧化钠滴定法从氯化铝溶液中制备氧化铝及其性能对比研究[J].有色金属科学与工程,2019,(04):19.
 Han Xiuxiu,Zhang Tingan,Lv Guozhi,et al.Research on alumina preparation from aluminum chloride solution[J].,2019,(04):19.

备注/Memo

备注/Memo:
收稿日期:2019-03-27
基金项目:国家自然科学基金资助项目(U1710257)
通信作者:张廷安(1960- ),男,教授,博导,主要从事自蔓延冶金,冶金反应工程学,高压湿法冶金等方向的研究,E-mail:zta2000@163.net.
更新日期/Last Update: 2019-08-22